Spandex fiber is the abbreviation of polyurethane fiber. The trade names include Lycra (Lycra, the United States, the United Kingdom, the Netherlands, Canada, Brazil), neolon (neolon, Japan), dorlastan (dorlastan, Germany), etc. Firstly, it was successfully studied by German Bayer company in 1937, and American DuPont company began industrial production in 1959. At present, there are nearly 40 factories and seven lines of production, with a total annual output of about 100000 tons, and China's existing production capacity of about 10000 tons. Spandex is a kind of synthetic fiber, which contains more than 85 percent polyurethane.
Der er to varianter af spandexfibre, den ene er mosaikcopolymeren af aromatisk diisocyanase og polyestersegment indeholdende hydroxyl (i det følgende benævnt polyesterspandex), og den anden er mosaikcopolymeren af aromatisk diisocyanat og polyethersegment indeholdende hydroxyl (i det følgende benævnt polyether spandex). Spandexfiber, elastisk polyolefinfiber og elastisk kompositfiber omtales tilsammen som elastisk fiber.
Syntetisk fiber med høj brudforlængelse (mere end 400 procent), lavt modul og høj elastisk genopretning. Kinesisk handelsnavn for multiblok polyurethanfiber. Også kendt som elastisk fiber. Spandex har høj forlængelse (500 procent 700 procent), lavt elasticitetsmodul (200 procent forlængelse, 0,04 0,12 g/Dan) og høj elastisk genopretning (200 procent forlængelse, 95 procent 99 procent). Ud over høj styrke ligner andre fysiske og mekaniske egenskaber meget naturlig latexsilke. Det er mere modstandsdygtigt over for kemisk nedbrydning end latextråd, har medium termisk stabilitet, og blødgøringstemperaturen er over 200 grader. De fleste farvestoffer og efterbehandlingsmidler, der anvendes til syntetiske og naturlige fibre, er også velegnede til farvning og efterbehandling af spandex. Spandex er svedbestandig, havvandsbestandig og modstandsdygtig over for forskellige rensemidler og de fleste solcremer. Langtidseksponering for sollys eller klorblegemiddel vil også falme, men falmningsgraden varierer meget med typen af spandex.
Spandex fiber has such high elasticity because its polymer chain is composed of low melting point and amorphous "soft" segments as the matrix and high melting point and crystalline "hard" segments embedded in it. Flexible chain segments form a certain network structure by certain cross{{0}}linking between molecular chains. Due to the small interaction force between molecular chains, they can stretch freely, resulting in large elongation. The molecular linkage force of rigid segment is relatively large, and the molecular chain will not elongate indefinitely, resulting in high resilience. Most of the cross sections of radon fiber filaments are dog bone shaped, and some filaments have smooth or serrated surfaces. The breaking strength is the lowest among all textile fibers, only 0.44 0.88cn/dtex (the strength of polyether type is higher than that of polyester type). The moisture absorption range is small, generally 0.3-1.2 percent (the moisture absorption rate of multifilament is slightly higher than that of monofilament). The heat resistance varies greatly depending on the variety. Most fibers are stored in the range of 90 150 degree for a short time, and the fibers will not be damaged. The safe ironing temperature is below 150 degree , which can be heated and wet washed. It has excellent dyeing performance and can be dyed into various colors. The dyes have strong affinity for fiber, can adapt to most kinds of dyes, and has good chemical resistance, resistance to most acid and alkali, chemicals, organic solvents, dry cleaners and bleaches, as well as resistance to sunlight and wind and snow, but not oxide, which is easy to turn yellow and reduce the strength of fiber.
Spandex bruges generelt ikke alene, men en lille mængde blandes i stoffet. Denne slags fiber har både gummi- og fiberegenskaber. De fleste af dem bruges i kernespundet garn med spandex som kernegarn, som kaldes elastisk kernespundet garn. De vigtigste egenskaber ved dette garn er som følger: For det første kan det opnå en god håndfølelse og udseende, og den eksterne fiber, der er sammensat af naturfibre, har en god fugtabsorption; For det andet kan kun 1-10 procent spandexfilament producere elastisk garn af høj kvalitet; For det tredje er kontrolområdet for elastikprocent fra 10 procent til 20 procent, og forskellige elastiske værdier kan vælges i henhold til produktets formål. Det er nemt at spinde 25 2500 denier silke af forskellig tykkelse, så det er meget brugt til at lave elastiske vævede stoffer, såsom strømpemund, møbelbetræk, skitøj, sportstøj, medicinske stoffer, bælter, Quartermaster-udstyr, elastiske dele af rumfart tøj osv. Efterhånden som folk fremsætter nye krav til stoffer, såsom let vægt, behagelig pasform og blød tekstur, stiger andelen af lavdenier spandex-stoffer også i syntetiske fiberstoffer. Det bruges også som snoet garn dannet af kombinationen af spandex nøgen silke og spandex og andre fibre. Det bruges hovedsageligt til alle former for kædestrikkede og skudstrikkede stoffer, vævede stoffer og elastiske stoffer.